| Specific Gravity | 1.06 | 1.06 | ASTM D 792 |
| Density | 1.06 | 0.0383 lb/in3 | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.0600 % | 0.0600 % | 23°C/50% RH; ISO 62 |
| Water Absorption at Saturation | 0.230 % | 0.230 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00500 - 0.00700
cm/cm @Thickness 3.20 mm | 0.00500 - 0.00700 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 20.0 g/10 min @Load 3.80 kg, Temperature 280 °C | 20.0 g/10 min @Load 8.38 lb, Temperature 536 °F | Melt Volume Rate (cm^3/10 min); ISO 1133 |
| 21.0 g/10 min @Load 3.80 kg, Temperature 280 °C | 21.0 g/10 min @Load 8.38 lb, Temperature 536 °F | ASTM D 1238 | |
| Hardness, Rockwell R | 106 | 106 | ISO 2039-2 |
| Tensile Strength at Break | 37.0 MPa | 5370 psi | 50 mm/min; ISO 527 |
| 39.0 MPa | 5660 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
| 35.0 MPa | 5080 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 40.0 % | 40.0 % | 50 mm/min; ISO 527 |
| 40.0 % | 40.0 % | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Yield | 2.30 % | 2.30 % | 50 mm/min; ISO 527 |
| 2.60 % | 2.60 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 1.85 GPa | 268 ksi | 1 mm/min; ISO 527 |
| 1.90 GPa | 276 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Modulus | 1.85 GPa | 268 ksi | 2 mm/min; ISO 178 |
| 2.10 GPa | 305 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Yield Strength | 52.0 MPa | 7540 psi | 2 mm/min; ISO 178 |
| 60.0 MPa | 8700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Charpy Impact, Notched | 0.600 J/cm2 @Thickness 4.00 mm, Temperature -30.0 °C | 2.86 ft-lb/in2 @Thickness 0.157 in, Temperature -22.0 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.10 J/cm2 @Thickness 4.00 mm, Temperature 23.0 °C | 5.24
ft-lb/in2 @Thickness 0.157 in, Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Impact Test | 27.0 J | 19.9 ft-lb | Instrumented Impact Total Energy; ASTM D 3763 |
| Taber Abrasion, mg/1000 Cycles | 90.0 | 90.0 | CS-17, 1 kg; SABIC Method |
| Izod Impact, Notched | 1.00 J/cm @Temperature -30.0 °C | 1.87 ft-lb/in @Temperature -22.0 °F | ASTM D 256 |
| 1.50 J/cm @Temperature 23.0 °C | 2.81
ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 @Thickness 4.00 mm, Temperature -30.0 °C |
3.33 ft-lb/in2 @Thickness 0.157 in, Temperature -22.0 °F | 80*10*4; ISO 180/1A |
| 9.00 kJ/m2 @Thickness 4.00 mm, Temperature 23.0 °C | 4.28
ft-lb/in2 @Thickness 0.157 in, Temperature 73.4 °F | 80*10*4; ISO 180/1A | |